Evaluation and comparison of anti-Candida effect of heat cure polymethylmethacrylate resin enforced with silver nanoparticles and conventional heat cure resins: An in vitro study.

Recent years have been dominated by research in nano science. Dentistry is no exception and there is increased research on nanoparticles in dentistry. Complete dentures increase the carriage of Candida in healthy patients, and the proliferation of C. albicans can be associated with denture-induced stomatitis. Purpose: To evaluate the anti-Candida effect of heat cure denture base resins reinforced with Ag° in the ratio of 4:1, 3:1, 2:1 (Groups B, C, and D, respectively) to the weight of denture base resins. Materials and Methods: Ag° were synthesized by chemical reduction method, incorporated into the polymer powder according to the ratio for each group, subjected to polymerization and microbial assay was calculated for the reference C. albicans strains by agar diffusion method for the incubation period of 24 h. Results: Group D showed multifold decrease in the colony-forming units. Conclusion: The antimicrobial effect of silver could be used vividly in the denture base for immunocompromised and geriatric patients.

Comparative evaluation of effect of laser on shear bond strength of ceramic bonded with two base metal alloys: An in-vitro study.

The most common clinical failure in metal ceramic restoration is at the ceramo-metal interface. For the clinical longevity, metal-ceramic prostheses must have satisfactory bond strength between metal and ceramic. Aim and Objective: The aim of this study is to evaluate the effect of Laser etching on shear bond strength between base metal alloys and ceramic. Materials and Methods: A total of 60 specimens were made (Base 5 mm diameter and 1 mm thickness, step with 4 mm diameter and 4 mm in length). They were divided into three groups. Group A-control, Group B-sand blasting, and Group C-laser etching. The Surface morphology, surface roughness, and wettability of the specimens were observed under scanning electron microscope (SEM) Ceramic application was carried out layer by layer for an optimal height of 4 mm. The shear bond strength test was performed using a universal testing machine and the nature of the fracture was examined under SEM. Results: The mean shear bond strength values for laser etched (Group C) Nickel-chromium (Ni-Cr) alloy bonded with ceramic was (49.12 ± 7.12 MPa) and ceramic bonded with Cobalt-chromium (Co-Cr) was (50.04 ± 4.27 MPa), sand blasted (Group B) Ni-Cr alloy bonded with ceramic was (26.00 ± 5.22 MPa), and ceramic bonded with Co-Cr was 24.54 ± 4.78 MPa. The SEM image after debonding showed 10% of adhesive failure and 70% cohesive failure and 20% of both adhesive and cohesive failure for Laser etching. However, there was no significant difference in the values of shear bond strength between the two base metal alloys in Group C. Conclusion: The s hear bond strength between ceramic bonded with Ni-Cr alloys using the Laser etching as surface treatment was 49.12 ± 7.12 MPa and for Co-Cr alloys 50.04 ± 4.27 MPa. Laser surface treatment produces an excellent surface roughness and achieved good shear bond strength values and aid in achieving a better bond strength between metals and ceramic.

Comparison of obturator design for acquired maxillary defect in completely edentulous patients.

The most challenging and appreciated area in the field of Prosthodontics is the rehabilitation of maxillary defects. Tumors of the head and neck are the common cause for acquired maxillofacial defects. Surgical consequences predispose the patient to hypernasal speech, fluid leakage into nasal cavity, impaired masticatory function, and cosmetic deformity. The Prosthodontists play a significant role in the intervention and improve the quality of life of such patients. The current article describes two clinical case reports of completely edentulous patients with acquired maxillary defects.